Established in Oct. 2010, BAYGOLD Group is a leading enterprise devoting to rubber technology industry.
Through years development, the company has grown into an integrated group that covers tire design, manufacturing of tire wire, tire cord fabric, rubber chemical and other tire materials.
Till 2018, the group now has an annual output of 5.8 million sets of all-steel truck radial tires, 24 million sets of passenger car tires, 10,000 tons of rubberized steel cord, 150,000 tons tire wire, 30,000 tons fabric (including 1,000 tons chafer fabric and 1,000 tons liner tire fabric), 1 million meters rubber hoses.
While actively expanding the domestic market. Group is also vigorously busy in exploring the international market. The products have been exported to more than 100 countries including Europe, America, Middle East, Africa, Southeast Asia. With excellent quality and complete after-sales service, the company has won the trust of customers, and enjoys a high reputation in the domestic and foreign market.
In order to accelerate the development and all-around better serve our customer, BAYGOLD group has invested 6,000 square meters of warehouses to operate logistic & storage business.
Future BAYGOLD group will become large comprehensive enterprise group that integrates production, technical research, industry and trade.
BAYGOLD group will continue taking the road of brand development by duty and loyalty in wide areas, and try our best to serve for our customers.
|
TECHNICAL SPECIFICATIONS OF NYLON-6 DIPPED TYRE CORD FABRIC
|
|
CORD CONSTRUCTION
|
UNIT
|
930dtex/1
(840D/1)
|
1400dtex/1
(1260D/1)
|
1870dtex/1
(1680D/1)
|
930dtex/2
(840D/2)
|
1400dtex/2
(1260D/2)
|
1400dtex/3
(1260D/3)
|
1870dtex/2
(1680D/2)
|
2100dtex/2
(1890D/2)
|
|
TENSILE STRENGTH
|
N
|
≥70
|
≥103
|
≥132
|
≥133
|
≥206
|
≥304
|
≥270
|
≥304
|
|
ELONGATION
|
|
|
|
|
|
|
|
|
|
|
AT 100N(10.2KG)
|
%
|
|
|
|
|
|
9.0±1.0
|
|
9.0±1.0
|
|
AT 88.2N(9KG)
|
%
|
|
|
|
|
|
|
9.0±1.0
|
|
|
AT 66.6N(6.8KG)
|
%
|
|
|
|
|
9.0±1.0
|
|
|
|
|
AT 44.1N(4.5KG)
|
%
|
11.0±1.0
|
|
8.0±1.0
|
9.0±1.0
|
|
|
|
|
|
AT 33N(3.4KG)
|
%
|
|
8.0±1.0
|
|
|
|
|
|
|
|
ADHESION (H-TEST)
|
N/CM
|
≥65
|
≥75
|
≥88
|
≥120
|
≥157
|
≥172
|
≥166
|
≥172
|
|
CORD GUAGE
|
MM
|
0.32±0.03
|
0.39±0.03
|
0.45±0.03
|
0.53±0.03
|
0.64±0.03
|
0.78±0.03
|
0.74±0.03
|
0.78±0.03
|
|
DIP PICK UP
|
%
|
4.2±1.0
|
4.2±1.0
|
4.2±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
|
ELONGATION AT BREAK
|
%
|
21±2
|
20±2
|
20±2
|
22±2
|
23±2
|
23±2
|
23±2
|
23±2
|
|
MOISTURE CONTENT
|
%
|
≤1.0
|
≤1.0
|
≤1.0
|
≤1.0
|
≤1.0
|
≤1.0
|
≤1.0
|
≤1.0
|
|
HEAT SHRINKAGE
(160℃, 2Mins.)
|
%
|
≤5
|
≤5
|
≤5
|
≤6
|
≤6
|
≤6
|
≤6
|
≤6
|
|
FABRIC WIDTH
|
CM
|
CM±1
|
CM±1
|
CM±1
|
CM±1
|
CM±1
|
CM±1
|
CM±1
|
CM±1
|
|
WEFT DENSITY
|
END/10CM
|
8--10
|
8--10
|
8--10
|
8--10
|
8--10
|
8--10
|
8--10
|
8--10
|